Products Description
Magnesite-ferrum spinel brick and synthetic magnesite-ferrum-alumina spinel brick are made of high purified magnesite clinker and ferrum-alumina spinel clinker at strictly controlled temperature and sintered atmosphere,which enables the product to have good flexibility and temperature vibration. The performances of attaching kiln wall and corrosion resistance are better good quality magnesite chrome brick.the product is update product for lining of large dry cement rotary kilns.
Products Specifications
| Items | Index | |||
| ZA-1 | ZA-2 | ZA-3 | ||
| Chemical Composition | MgO, % ≥ | 88 | 86 | 85 |
| Fe2O3 % | 3-5 | 5-7 | 3-5 | |
| Al2O3 % | 3-5 | 1.0 | 1.0 | |
| SiO2 % ≤ | 1.0 | 1.0 | 1.0 | |
| Bulk Density(g/cm3) | 2.95 | 2.95 | 2.95 | |
| Apparent Porosity, % ≤ | 16 | 16 | 16 | |
| Cold Crushing Strength, MPa ≥ | 80 | 80 | 80 | |
| Refractoriness Under Load,°C, [0.2MPa×0.6%] ≥ | 1700 | 1650 | 1680 | |
| hermal Shock Resistance, Times, [1100°C, water-cooling] | 10 | 8 |
10
|
|
Refractory bricks are essential for protecting the kiln or furnace shell from heat, wear, and chemical erosion, ensuring the longevity and efficiency of the equipment. They are also commonly used as insulation materials to reduce energy loss and improve the overall performance of high-temperature equipment.