One of the main advantages of ferro-vanadium 10-50 mm is its strength. It is a very hard and durable material that is resistant to wear and tear.

Send Inquiry

Product Introduction

60% Ferro Vanadium 10-50 Mm Description

One of the main advantages of ferro-vanadium 10-50 mm is its strength. It is a very hard and durable material that is resistant to wear and tear. This makes it ideal for use in the production of high-quality tools, equipment, and even vehicles. Ferrovanadium is also able to withstand high temperatures and pressures.

product-500-500

60% Ferro Vanadium 10-50 Mm Composition

Chem. element	C	Si	Mn	S	P	V	Al	Cu	As
Mass. % up to	0,5	2	4	0,02	0,07	60	0,3	0,2	0,01

Ferrovanadium is produced in several ways:

The main method of obtaining the alloy is silicothermal (silico-aluminothermic). In the smelting process, vanadium pentoxide is first obtained from the ore, which is then reduced in an electric furnace using silicon or aluminum.

The hydrometallurgical method is used when the vanadium content in titanium-magnesium ore is high. The iron-vanadium concentrate is rounded or subjected to agglomeration, obtaining vanadium pentoxide.

In the pyrometallurgical process, vanadium is obtained from cast iron formed after the agglomeration of iron-vanadium concentrate. Cast iron is oxidized in a converter, obtaining slag with 10% vanadium.